Cerium (IV) oxide*
- Formula
- CeO2
- Refraction index (at λ=550 nm)
- 2,0
- Transparency range, µm
- 0,4-16
- Density, g/sm
- 5,5-7,1
- Recommended evaporation temperature, °С
- 2000
- Product form, dimensions (mm)
- tablets
Ø 12-25, h 5-15
granules 1-10
Properties (oxides)
Material | Formula | Refraction index (at λ=550 nm) | Transparency range, µm | Density, g/sm | Recommended evaporation temperature, °С | Product form, dimensions (mm) |
---|---|---|---|---|---|---|
Aluminium oxide | Al2O3 | 1,63 | 0,2-7 | 3,9-4,0 | 2000-2200 | granules 1-10 |
Cerium (IV) oxide* | CeO2 | 2,0 | 0,4-16 | 5,5-7,1 | 2000 | tablets Ø 12-25, h 5-15 granules 1-10 |
Europium oxide* | Eu2O3 | 1,9 | 0,26-9 | 5,5-7,4 | 2300-2500 | tablets Ø 12-25, h 5-15 |
Gadolinium (III) oxide* | Gd2O3 | 1,8 | 0,22->1 | 5,5-7,4 | 2300-2500 | tablets Ø 12-25, h 5-15 |
Hafnium (IV) oxide | HfO2 | 1,9-2,07 | 0,23-8 | 6,5-9,7 | 2300-2500 | tablets Ø 12-25, h 5-15 granules 1-10 |
Indium (III)-Tin (IV) oxide | In2O3SnO2 | 1,82-1,95 | 0,4-1,1 | 4,0-7,1 | tablets Ø 12-25, h 5-15 | |
Magnesium oxide | MgO | 1,65-1,77 | 0,2-8 | 2,5-3,6 | 2300-2500 | tablets Ø 12-25, h 5-15 |
Niobium (V) oxide | Nb2O5 | 2,2-2,4 | 0,42-8 | 3,5-4,5 | 1800-1900 | tablets Ø 12-25, h 5-15 granules 1-10 |
Silicon (IV) oxide | SiO2 | 1,46 | 0,2-9 | 1,8-2,2 | 1800-2200 | Ø 12-25, h 5-15 granules 1-10 |
Tantalum (V) oxide | Ta2O5 | 2,0-2,1 | 0,3-10 | 6,0-8,3 | 1900-2200 | tablets Ø 12-25, h 5-15 granules 1-10 |
Tin (IV) oxide | SnO2 | 2,0 | 0,4-9 | 4,0-6,7 | tablets Ø 12-25, h 5-15 | |
Titanium (II) oxide | TiO | 2,4 | 0,4-7 | 3,5-4,9 | 1700-2000 | granules 1-10, tablets Ø 12-18, h 8-12 |
Titanium (IV) oxide | TiO2 | 2,2-2,4 | 0,4-7 | 3,0-4,2 | 2000-2200 | tablets Ø 12-25, h 8-12 granules 1-10 |
Titanium oxide | Ti3O5 | 2,2-2,4 | 0,4-7 | 3,0-4,6 | 2000-2200 | tablets Ø 12-25, h 8-12 granules 1-10 |
Yttrium oxide | Y2O3 | 1,79-1,85 | 0,25-12 | 3,5-5,0 | 2300-2500 | tablets Ø 12-25, h 5-15 |
Zirconium (IV) oxide | ZrO2 | 1,97-2,1 | 0,35-7 | 4,6-5,6 | 2500 | tablets Ø 12-25, h 5-15 granules 1-10 |